Study on Effect of Moisture Content of Semi-Gloss Polyester FDY Chips on Filament Quality and Fabric Properties
作者:
王 敏;  戴伟波;  施寄青;  索俊伟;  赵 爽
吴江佳力高纤有限公司,江苏 苏州 215228
Author(s):
WANG Min;  DAI Weibo;  SHI Jiqing;  SUO Junwei;  ZHAO Shuang
Wujiang Jiali Advanced Fiber Co.,Ltd.,Suzhou 215228,China
分类号:
TS 941.41
文献标志码:
A
摘要:
为改善长丝面料的平整度与色差问题,从长丝原料出发,采用单因素法探讨了聚酯切片含水率对长丝断裂强度、条干均匀度以及织物面料的影响。实验表明:在纺制22.2 tex/48F半光涤纶FDY的过程中,切片含水率为30 mg/L时,涤纶FDY的断裂强度和条干均匀度为最佳,即长丝质量达到最优; 为保证切片含水率在30 mg/L,干燥温度和干燥时间分别为135 ℃与4 h最合理。用半光涤纶FDY织造的面料布面平整光滑,染色后无色档,优于市场上同规格产品,具有一定的市场应用价值。
Abstract:
In order to improve the flatness and color difference of fabrics made by filament, the influence of moisture content of polyester FDY chips on the breaking strength,evenness and fabric properties was studied by single factor method. The experimental results showed that: in the spinning process of 22.2 tex/48F semi-gloss polyester FDY, when the moisture content of chips is 30 mg/L, the full-package rate of polyester FDY is the best. The breaking strength and evenness of polyester FDY are the best, that is, the quality of filaments is the best. In order to ensure 30 mg/L moisture content for chips the drying temperature and drying time are most reasonable at 135 ℃ and 4 h, respectively. The fabrics woven with these filaments have smooth surface and no color file after dyeing, which is superior to the same specification products on the market and has certain market application value.

参考文献/References:

[1] 王连军,姚荣兴,黄象安.粗旦丙纶长丝不匀率的影响因素分析[J].合成纤维工业,2004,27(4):44- 46.
WANG Lianjun, YAO Rongxing, HUANG Xiang’an. Analysis of influential factors on yarn irregularity of coarse denier PP filament[J]. China Synthetic Fiber Industry, 2004,27(4):44- 46.(in Chinese)
[2] 徐心华,李允成. 涤纶长丝生产[M].北京:纺织工业出版社,1989:14-26.
[3] 彭凤信.尼龙66切片干燥工艺的优化[J].纺织导报,2014(4):58- 60.
PENG Fengxin. Optimization of drying process of PA66 chips[J]. China Textile Leader, 2014(4):58- 60.(in Chinese)
[4] 夏修成.聚酯切片干燥工艺与流程的优化[J].金山油化纤,1990(2):36-39.
XIA Xiucheng. Optimization of process and drying technology of polyester chips[J]. Petrochemical Technology in Jinshan, 1990(2):36-39.(in Chinese)
[5] 王亚丽,周微伟.熔融纺丝法中聚乳酸切片干燥工艺探讨[J].天津纺织科技,2009(4):11-14.
WANG Yali, ZHOU Weiwei. Discussion on the drying process of polylactic acid chips in melt spinning[J]. Tianjin Textile Science and Technology,2009(4):11-14.(in Chinese)
[6] 张建祥,刘淑云,耿彩花,等.整理方式对纯棉色织面料折皱回复角和平整度的影响[J].染整技术,2016,38(1):14-16.
ZHANG Jianxiang, LIU Shuyun, GENG Caihua, et al.The influence of finishing method on crease recovery angle and appearance smoothness for cotton yarn-dyed fabric[J]. Textile Dyeing and Finishing Journal, 2016,38(1):14-16.(in Chinese)
[7] 唐友荣,刘德威.聚酯切片干燥性能研究[J].聚酯工业,1996(3):40- 43.
TANG Yourong, LIU Dewei. Study on drying properties of polyester chips[J]. Polyester Industry, 1996(3):40- 43.(in Chinese)
[8] 陈慧敏. 基于点模型的服装面料平整度等级客观评级研究[D].上海:东华大学,2007.
(责任编辑:张 雪,邢宝妹)

更新日期/Last Update: 2018-12-28